Property
|
Method
|
Value
|
Units
|
|
Physical Properties |
|
|
|
Density |
ISO
1183 |
1410 |
kg/m^3 |
|
Melt volume rate (MVR) |
ISO
1133 |
8.5 |
cm^3/10min |
|
Mold shrinkage - parallel |
ISO
294-4 |
2.2 |
% |
|
Mold shrinkage - normal |
ISO
294-4 |
2.0 |
% |
|
Water absorption (23°C-sat) |
ISO
62 |
0.65 |
% |
|
Humidity absorption (23°C/50%RH) |
ISO
62 |
0.2 |
% |
| |
|
Mechanical Properties |
|
|
|
|
Tensile modulus (1mm/min) |
ISO
527-2/1A |
2780 |
MPa |
|
Tensile stress at yield (50mm/min) |
ISO
527-2/1A |
66 |
MPa |
|
Tensile creep modulus 1h |
ISO
899-1 |
2450 |
MPa |
|
Tensile creep modulus 1000h |
ISO
899-1 |
1350 |
MPa |
|
Flexural modulus (23°C) |
ISO
178 |
2640 |
MPa |
|
Charpy notched impact strength @ 23°C |
ISO
179/1eA |
5.8 |
KJ/m^2 |
|
Notched impact strength (Izod) @ 23°C |
ISO
180/1A |
5.5 |
KJ/m^2 |
| |
|
Thermal Properties |
|
|
|
|
Melting temperature (10 C/min) |
ISO 11357-1,-2,-3 |
165 |
°C |
|
DTUL @ 1.8 MPa |
ISO
75-1, -2 |
100 |
°C |